Fatigue Crack Striation Spacing for Welded and Base Material CT Steel Specimens

• Tipo: Artigo em Livro de Atas de Conferência Internacional
• Data: 2013

Autores

Richter Trummer, V (Autor) Outra; Miranda, RMC (Autor) Outra; Albuquerque, C (Autor) Outra; Paulo Tavares de Castro (Autor) FEUP

Ata de Conferência Internacional

Título: ADVANCED MATERIALS FORUM VI, PTS 1 AND 2

Páginas: 793-798

6th International Materials Symposium (MATERIALS 2011)/15th Meeting of SPM

Guimaraes, PORTUGAL, APR 18-20, 2011

Indexação

ISI Web of Knowledge - 0 Citações

Scopus - 2 Citações

Outras Informações

ID Authenticus: P-005-3Q0

DOI: 10.4028/www.scientific.net/msf.730-732.793

Abstract (EN): Scanning electron microscopy (SEM) observation of the fracture surface of CT specimens was carried out at CEMUP in the context of a FEUP R&D programme for the characterization of fatigue crack growth (FCG) of base material and welded steel CT specimens, carried out under constant load range, reported in a companion paper. The inclusion of specimens of welded material in the FCG characterization programme justified the need for relatively large size specimens. The thickness of the specimens (B=32mm) was approximately identical to the thickness of the structural application of interest, since with thinner specimens the possible effects of residual stress fields would be at least partially lost. The CT specimens were designed according to ASTM E647 standard. The FEI QUANTA 400 FEG / EDAX Pegasus X4M available at CEMUP was used for the SEM observations, carried out in the fatigue fracture surfaces of base and welded (HAZ) steel: Both in base material as well as in welded specimens, it was found that there are regions of the fracture surfaces where no striations are observed, mixed with other regions (patches) with striations. Some regions are featureless (ropey appearance). It was not possible to find a preferential orientation of the striation spacing, that might be directly related with the macroscopic direction of crack propagation; on the contrary, the regions presenting striations seem to have a mainly random orientation. This fact contributes to the absence of correlation between the distance between striations (s) measured using SEM, and the macroscopic fatigue crack growth rate da/dN. Only for substantial values of the crack length/specimen width (a/W) ratio a reasonable agreement between s and da/dN is found. The relationship s/(da/dN) presents values that decrease up to approximately one, as a/W increases. For low values of a/W, s is one or two orders of magnitude greater than da/dN. In the specimens analyzed, fatigue crack growth rates below approximately 2 to 3 x10(-7) m/cycle are associated with approximately constant s values. This border is over the transition between regions I and II of the typical sigmoidal log-log plot of the da/dN vs. Delta K (I corresponding to the near threshold regime and II to the Paris law regime), and this fact should be accounted for in failure analysis involving SEM of fracture surfaces. Finally, the distance between striations s proved to be insensitive to the presence of important residual stresses in the case of the welded specimens.