Photocatalytic performance of Au/ZnO nanocatalysts for hydrogen production from ethanol

• Tipo: Artigo em Revista Científica Internacional
• Data: 2016

Autores

Maria J. Sampaio (Autor) FEUP; João W. L. Oliveira (Autor) Outra; Caroline I. L. Sombrio (Autor) Outra; Daniel L. Baptista (Autor) Outra; Sérgio R. Teixeira (Autor) Outra; Sónia A. C. Carabineiro (Autor) FEUP; Cláudia G. Silva (Autor) FEUP; Joaquim L. Faria (Autor) FEUP

Revista

Título: Applied Catalysis A: General

Vol. 518

Páginas: 198-205

ISSN: 0926-860X

Editora: Elsevier

Indexação

ISI Web of Knowledge - 26 Citações

Scopus - 43 Citações

Projetos Associados

LSRE-LCM - Laboratório de Processos de Separação e Reação - Laboratório de Catálise e Materiais

Outras Informações

ID Authenticus: P-00K-MQT

DOI: 10.1016/j.apcata.2015.10.013

Abstract (EN): Gold was loaded on several ZnO samples with different morphologies: needle-like (ZnO-n), flower-like (ZnO-f), rods (ZnO-r), and prepared by a thermal calcination process (ZnO-t). A commercial ZnO sample (ZnO-c) was also used for comparison. Bare ZnO and Au/ZnO materials were used for the photocatalytic production of H2 from a water-ethanol solution under UV-vis irradiation (¿ > 300 nm). During the photocatalytic runs, hydrogen was generated at a constant rate for all samples, as well as CH4 and CO. The obtained results show that bare ZnO materials were able to promote H2 photogeneration, being ZnO-f the most efficient in terms of H2 generation. Loading with Au, in general, increased the photoefficiency for all materials. The most active gold loaded photocatalysts were the ones with the lowest gold nanoparticle sizes: Au/ZnO-f (427 ¿mol h-1 gcat -1; 5.4 nm) and Au/ZnO-n (280 ¿mol h-1 gcat -1; 5.8 nm). The samples with largest size (Au/ZnO-r and Au/ZnO-t with 6.2 nm, and Au/ZnO-c with 12.5 nm) were not so efficient (values below 230 ¿mol h-1 gcat -1). Au/ZnO-f seems to be the most promising photocatalyst, generating the highest amount of H2 and the lowest quantities of CH4 and CO. It is also possible that the intricate morphology of ZnO-f may scatter the incoming light, enhancing light absorption efficiency and increasing the photoefficiency of this material.