Mixed-mode I plus II fracture characterisation of composite bonded joints

• Tipo: Artigo em Revista Científica Internacional
• Data: 2020

Autores

Marcelo F. S. F. de Moura (Autor) FEUP; Raul D. F. Moreira (Autor) FEUP; Filipe G.A. Silva (Autor) FEUP; Francis M. G. Ramirez (Autor) FEUP; J. S. Rodrigues (Autor) Outra

Revista

Título: Journal of Adhesion Science and Technology

Vol. 34

Páginas: 1385-1398

ISSN: 0169-4243

Editora: Taylor & Francis

Indexação

ISI Web of Knowledge - 0 Citações

Scopus - 2 Citações

Classificação Científica

CORDIS: Ciências Tecnológicas > Engenharia > Engenharia mecânica

FOS: Ciências da engenharia e tecnologias > Engenharia mecânica

Outras Informações

ID Authenticus: P-00R-NXV

DOI: 10.1080/01694243.2019.1708645

Abstract (EN): This work addresses fracture characterisation of composite bonded joints under mixed-mode I+II loading. A proper strategy, including only two different loading conditions applied to five tests, is performed to obtain the fracture law describing the mixed-mode fracture behaviour. The peel test loading condition is employed to characterise fracture under pure mode I loading considering a symmetrical double-cantilever beam specimen and under mixed-mode I+II with mode I supremacy with an asymmetrical double-cantilever beam specimen. Three-point bending loading condition was also employed. The end-notched flexure test was used to characterise fracture under pure mode II, while the asymmetric single-leg bending tests were performed to cover mixed-mode I+II loading with mode II predominance up to a mode-mixity with moderate mode I prevalence. A methodology using cohesive zone modelling was applied to perform loading mode partition, which is crucial for an appropriate identification of the criterion describing the fracture behaviour of these joints.