Production of water tolerant melamine-urea-formaldehyde resin by incorporation of sodium metabisulphite

• Tipo: Artigo em Revista Científica Internacional
• Data: 2016

Autores

Nádia T. Paiva (Autor) FEUP; João M. Ferra (Autor) FEUP; João Pereira (Autor) FEUP; Jorge Martins (Autor) FEUP; Luísa Carvalho (Autor) FEUP; Fernão D. Magalhães (Autor) FEUP

Revista

Título: International Journal of Adhesion and Adhesives

Vol. 70

Páginas: 160-166

ISSN: 0143-7496

Editora: Elsevier

Indexação

ISI Web of Knowledge - 7 Citações

Scopus - 7 Citações

INSPEC

Projetos Associados

LEPABE - Laboratório de Engenharia de Processos, Ambiente, Biotecnologia e Energia

Outras Informações

ID Authenticus: P-00K-MGR

DOI: 10.1016/j.ijadhadh.2016.06.005

Abstract (EN): The aim of this work was the development of a new MUF resin formulation with high tolerance towards water dilution, and a good overall performance in terms of physico-mechanical properties and formaldehyde emissions. For this purpose, sodium metabisulphite (MTBS) was added during melamine condensation reaction, therefore decreasing its extent by blocking amino groups. It was found that the resins with higher amounts of MTBS have obtained the higher water dilution capacity (a percentage of 6% of MTBS resulted in a resin with a water tolerance about 60 times higher than the one present in a resin without MTBS incorporation). The molecular weight distribution showed that the resins produced with MTBS have a different polymeric structure. Regarding particleboard production and evaluation, it was possible to conclude that the increase in MTBS addition lowers the internal bond strength and formaldehyde emissions. However, with the resin, having the MTBS addition of 6%, it was still possible to obtain the panel with internal bond strength higher than the acceptable minimum (0.45 N mm(-2)), with a pressing time of 150 s. When compared with commercial MUF resins, the formulation developed in this work presents lower values of formaldehyde emissions, complying to CARB II regulation, even though with somewhat inferior physico-mechanical performances.