Evaluation of SICON® surfaces for biofouling mitigation in critical process areas

• Type: Article in International Scientific Journal
• Date: 2016

Authors

J. M. R. Moreira (Author) FEUP; R. Fulgêncio (Author) FEUP; F. Oliveira (Author) FEUP; I. Machado (Author) FEUP; I. Bialuch (Author) Other; L. F. Melo (Author) FEUP; M. Simões (Author) FEUP; F. J. Mergulhão (Author) FEUP

Journal

Title: Food and Bioproducts Processing: Transactions of the Institution of of Chemical Engineers, Part C

Vol. 98

Pages: 173-180

ISSN: 0960-3085

Publisher: Institution of Chemical Engineers

Indexing

ISI Web of Knowledge - 2 Citations

ISI Web of Science

Scopus - 5 Citations

Associated Projects

SUSCLEAN - Sustainable Cleaning and Disinfection in Fresh-Cut Food Industries

LEPAE/CEFT - RL2 - (Bio) Chemical Engineering: Multi-Scale Approaches for Sustainable Environment and Health

LEPABE - Laboratório de Engenharia de Processos, Ambiente, Biotecnologia e Energia

Other information

Authenticus ID: P-00K-4TN

DOI: 10.1016/j.fbp.2016.01.009

Abstract (EN): In industrial processes, particularly in the food sector, sustainability is increasingly important. Consumers demand safer food and this is often associated with elevated cleaning costs and high environmental impacts in order to reduce contaminations on equipment and products. Modified surfaces are seen as a promising strategy for biofouling mitigation and contamination prevention. In this work, the performance of a modified Diamond-Like Carbon (DLC) surface designated by SICON® (a-C:H:Si:O) was compared with stainless steel (316L) regarding bacterial adhesion, biofilm formation and cleanability. Assays were performed at different temperatures using Escherichia coli, one of the most persistent foodborne microorganisms and also the natural flora present in the water from an industrial salad washing line. Bacterial adhesion on SICON® and stainless steel were similar and favored at a higher temperature (30 °C). Biofilm formation was reduced on SICON® (1-2 Log) and this may be explained by the lower ratio between the Lifshitz-van der Waals apolar component and the electron donor component (γLW/γ-) of this surface. It was also shown that after performing a cleaning treatment with chlorine, reduction of viability counts was much higher in SICON® (about 3.5 Log reduction and 15% removal) when compared to stainless steel (1.6 Log reduction and 6% removal). Additionally, it was observed that 18 h after treatment, biofilm values in SICON® were similar to those obtained with stainless steel. Results indicate that for industries with cleaning frequencies of up to 6 h, the use of SICON® on critical areas enables operation at a much higher hygienic level.