Vanadium (oxy)nitride as a new category of anode for direct ammonia solid oxide fuel cells cells

• Tipo: Artigo em Revista Científica Internacional
• Data: 2022-12

Autores

Laura Holz (Autor) Outra; Francisco Loureiro (Autor) Outra; Vanessa Graça (Autor) Outra; Sergey Mikhalev (Autor) Outra; Diogo Mendes (Autor) Outra; Adélio Mendes (Autor) FEUP; Duncan Fagg (Autor) Outra

Revista

Título: Renewable Energy

Vol. 201

Páginas: 124-130

ISSN: 0960-1481

Editora: Elsevier

Indexação

ISI Web of Knowledge - 0 Citações

Scopus

Outras Informações

ID Authenticus: P-00X-D0H

DOI: 10.1016/j.renene.2022.10.098

Abstract (EN): Ammonia (NH3) is considered a potential energy carrier to be used as a fuel in energy conversion devices, such as solid oxide fuel cells (SOFCs). Nonetheless, in the presence of NH3, traditional Ni-containing anodes may suffer from poor chemical stability, resulting in its partial conversion to nickel nitride. We, therefore, propose a new composite anode for direct ammonia solid oxide fuel cells made of a metallic conducting phase, vanadium (oxy) nitride (VON), and an oxygen-ion conducting phase, (ZrO2)(0.92)(Y2O3)(0.08) (YSZ). X-ray diffraction (XRD) reveals that the VON material is chemically compatible with YSZ. Good thermal stability was also shown under reducing conditions by thermogravimetry (TGA). Electrochemical impedance spectroscopy (EIS) showed that peak performing composition is composed of 50:50% vol of VON:YSZ at 850 degrees C, yielding comparable performance to that of previous reports on traditional Ni-YSZ cermets. The electrode mechanism under NH3 fuel was found to be similar to that of traditional Ni-based cermet compositions using hydrogen fuel, due to the predicted thermal decomposition of ammonia under the studied operation temperatures, i.e., >= 650 degrees C, while sensitivity to flow rate considerations was also highlighted. To the best of our knowledge, this work reports a completely new category of anodes for SOFC applications.