Characterization of electrodeposited Ni and Ni80Fe20 nanowires

• Tipo: Artigo em Revista Científica Internacional
• Data: 2008

Autores

leitao, d. c. (Autor) Outra; sousa, c. t. (Autor) Outra; ventura, j. (Autor) REIT; amaral, j. s. (Autor) Outra; carpinteiro, f. (Autor) Outra; pirota, k. r. (Autor) Outra; vazquez, m. (Autor) Outra; sousa, j. b. (Autor) FCUP; araujo, j. p. (Autor) FCUP

Revista

Título: Journal of Non-Crystalline Solids

Vol. 354 Nº 2585

Páginas: 5241-5243

ISSN: 0022-3093

Editora: Elsevier

Indexação

ISI Web of Knowledge - 15 Citações

Scopus - 18 Citações

Outras Informações

ID Authenticus: P-003-TK6

DOI: 10.1016/j.jnoncrysol.2008.05.088

Abstract (EN): In this work we use nanoporous alumina substrates as templates for the growth of Ni and Ni80Fe20 nanowires. Our membranes were obtained by a two-step anodization process of high-purity aluminum foils: first anodizations were performed at 40 V for 15 h in 0.3 M oxalic acid, at 2-6 degrees C; the second anodization was carried out using the same conditions for 30 min, resulting in pore lengths of similar to 1.3 mu m. After the second anodization, the pore bottom barrier-layer was thinned, to allow the current to flow through electron tunneling. A pulsed electrodeposition method was then used to grow Ni and Ni80Fe20 nanowires. Transport characterization and isothermal magnetization measurements performed on the produced arrays are presented.