Crystallisation studies of biodegradable CaO-P2O5 glass with MgO and TiO2 for bone regeneration applications

• Tipo: Artigo em Revista Científica Internacional
• Data: 2004

Autores

Anabela Dias (Autor) Outra; K. Tsuru (Autor) Outra; T. Hayakawa (Autor) Outra; Maria Ascensão Lopes (Autor) FEUP; José Domingos Santos (Autor) FEUP; A. Osaka (Autor) Outra

Revista

Título: Glass Technology

Vol. 45 Nº 2

Páginas: 78-79

ISSN: 0017-1050

Editora: Society of Glass Technology

Indexação

ISI Web of Knowledge - 9 Citações

Scopus - 9 Citações

Classificação Científica

FOS: Ciências da engenharia e tecnologias > Engenharia dos materiais

Outras Informações

ID Authenticus: P-000-AYS

Abstract (EN): CaO-P2O5 glass ceramics with small additions of MgO and TiO2 were prepared in the ortho and pyrophosphate regions by powder sintering and crystallisation through heat treatment at different temperatures determined from, differential thermal analysis (DTA). The glass ceramics were analysed by x-ray diffraction (XRD) and it was observed that alpha- and beta-Ca2P2O7 were the first phases to precipitate in the parent glass matrix at a temperature of 681degreesC, followed by CaTi4(PO4)(6) and TiP2O7 at temperatures between 703 and 725degreesC The beta-Ca2P2O7 and CaTi4(PO4)(6) phases are usually considered as biocompatible and bioactive and, therefore, these glass ceramics seem to show good potential for bone regeneration applications.