Tunnel magnetoresistance and magnetic ordering in ion-beam sputtered Co80Fe20/Al2O3 discontinuous multilayers

• Tipo: Artigo em Revista Científica Internacional
• Data: 2001

Autores

G.N. Kakazei (Autor) Outra; pogorelov, y. g. (Autor) FCUP; Lopes, AML (Autor) Outra; sousa, j. b. (Autor) FCUP; Cardoso, S (Autor) Outra; Freitas, PP (Autor) Outra; de Azevedo, MMP (Autor) Outra; Snoeck, E (Autor) Outra

Revista

Título: Journal of Applied Physics

Vol. 90

Páginas: 4044-4048

ISSN: 0021-8979

Editora: American Institute of Physics

Indexação

ISI Web of Knowledge - 78 Citações

Scopus - 80 Citações

Outras Informações

ID Authenticus: P-000-T10

DOI: 10.1063/1.1399029

Abstract (EN): Discontinuous multilayered Co80Fe20(t)/Al2O3(30 Angstrom) thin films have been prepared by ion-beam sputtering. We report on structural, magnetic, and transport (for current in plane geometry) results obtained in this system. With growing nominal thickness t of the metal layers, which effectively characterizes the granular structure, a transition from tunnel to metallic conductance is observed, indicating the onset of infinite conducting paths at t> 18 Angstrom. At t< 18 <Angstrom>, that is within the range of tunnel regime, a different characteristic value t> 13 Angstrom was detected from the magnetization data which display here a transition from superparamagnetic to ferromagnetic behavior. The measurements of tunnel magnetoresistance (MR) show that a sharp maximum of MR sensitivity to field takes place at this thickness, reaching similar to 24%/kOe at room temperature. At least, MR itself as a function of t has a break at the same value. All these features suggest that Some specific kind of percolation with respect to magnetic order occurs in our system when the disordered granular structure is still well separated, as confirmed by the data of high resolution transmission electron microscopy. Hence such magnetic percolation is clearly distinct from usual electrical percolation in these discontinuous layers. At the same time, the highest MR (similar to6.5% at room temperature) in this series is attained with decreasing t only at t = 10 Angstrom. (C) 2001 American Institute of Physics.