Proton electrolyte membrane properties and direct methanol fuel cell performance

• Tipo: Artigo em Revista Científica Internacional
• Data: 2005

Autores

Silva, V (Autor) Outra; Ruffmann, B (Autor) Outra; Silva, H (Autor) Outra; Gallego, Y (Autor) Outra; Adélio Mendes (Autor) FEUP; Luis Madeira (Autor) FEUP; Nunes, S (Autor) Outra

Revista

Título: Journal of Power Sources

Vol. 140 Nº 1

Páginas: 41-49

ISSN: 0378-7753

Editora: Elsevier

Indexação

ISI Web of Knowledge - 119 Citações

ISI Web of Science

Scopus - 137 Citações

COMPENDEX

Classificação Científica

FOS: Ciências da engenharia e tecnologias > Engenharia química

CORDIS: Ciências Tecnológicas

Outras Informações

ID Authenticus: P-00H-BQC

DOI: 10.1016/j.jpowsour.2004.08.012

Abstract (EN): This paper presents an evaluation of the zirconium oxide effects in sulfonated poly(ether ether ketone) (sPEEK) with sulfonation degree (SD) of 87%. A series of inorganic-organic hybrid membranes were prepared with a systematic variation of the zirconium oxide content via in situ zirconia formation (2.5, 5.0, 7.5, 10, 12.5 wt.%). This procedure enabled the preparation of proton electrolyte membranes (PEM) with a wide range of properties, which can be useful for evaluating the relationship between the PEM properties and the direct methanol fuel cell (DMFC) performance. The investigated properties are the proton conductivity, proton transport resistance, water uptake, water, methanol, oxygen, carbon dioxide and nitrogen permeability coefficients, morphology and elemental analysis. The results obtained show that the inorganic oxide network decreases the proton conductivity and water swelling. It is found that it leads also to a decrease of the water, methanol, carbon dioxide and oxygen permeability coefficients, an increase of the water/methanol selectivity and a decrease of the carbon dioxide/nitrogen and oxygen/nitrogen selectivities. In terms of morphology, it is found that in situ zirconium alkoxide hydrolysis enables the preparation of homogeneous membranes that present a good adhesion between inorganic domains and the polymer matrix.