Effect of Aging Heat Treatment in an Al-4008 Produced by Liquid Metal Printing

• Tipo: Artigo em Revista Científica Internacional
• Data: 2024

Autores

Ladeiro, CM (Autor) Outra; Nunes, FL (Autor) Outra; Trindade, MM (Autor) Outra; Costa, JM (Autor) FEUP

Revista

Título: U.Porto Journal of Engineering

Vol. 10

Páginas: 45-58

Editora: Universidade do Porto. Faculdade de Engenharia

Indexação

Scopus

Outras Informações

ID Authenticus: P-00Z-WKJ

DOI: 10.24840/2183-6493_0010-001_002060

Abstract (EN): In today¿s world, additive manufacturing (AM) is one of the most popular technologies and has the potential to revolutionize the manufacturing industry. As one of the most recent advances in this industry, liquid metal printing has a growing value in the engineering field. This study aims to evaluate the effect of two heat treatment conditions in an Al-4008 alloy produced by this technique in the microstructure and mechanical properties. It was concluded that the heat treatment (HT) enhances the Si particle coalescence and Fe-rich intermetallic compound precipitation, increasing the sample hardness significantly (50%). Density analysis showed a slight porosity decrease with HT. Tensile tests indicated heat-treated, same-directionally pulled samples exhibited brittleness compared to as-printed ones, while HT increased both yield strength (245 MPa) and ultimate tensile strength (294 MPa). © 2024, Universidade do Porto - Faculdade de Engenharia. All rights reserved.

Idioma: Inglês

Tipo (Avaliação Docente): Científica

Nº de páginas: 13