Partial replacement of melamine by benzoguanamine in MUF resins towards improved flexibility of agglomerated cork panels

• Tipo: Artigo em Revista Científica Internacional
• Data: 2018

Autores

Ana Antunes (Autor) Outra; Margarida Duarte (Autor) Outra; Nádia Paiva (Autor) Outra; João Ferra (Autor) Outra; Jorge Martins (Autor) Outra; Luísa Carvalho (Autor) FEUP; Ana Barros Timmons (Autor) Outra; Fernão D. Magalhães (Autor) FEUP

Revista

Título: International Journal of Adhesion and Adhesives

Vol. 87

Páginas: 142-150

ISSN: 0143-7496

Editora: Elsevier

Indexação

ISI Web of Knowledge - 11 Citações

Scopus - 11 Citações

INSPEC

Projetos Associados

2GAR - 2GAR - Resinas Amino de segunda Geração

LEPABE - Laboratório de Engenharia de Processos, Ambiente, Biotecnologia e Energia

Outras Informações

ID Authenticus: P-00P-RCF

DOI: 10.1016/j.ijadhadh.2018.10.004

Idioma: Inglês

Tipo (Avaliação Docente): Científica

Notas: Melamine-urea-formaldehyde (MUF) resins are highly effective adhesives for lignocellulosic materials. However, their high stiffness hinders applications where flexibility is desired. In this work, MUF resins were modified with benzoguanamine by partially replacing melamine in two different steps of the synthesis. The purpose was to obtain a less densely crosslinked, and hence more flexible, structure after cure. All modified MUF resins were characterized using gel permeation chromatography (GPC). Results suggest that benzoguanamine and its derivatives were integrated into the polymer structure. FTIR and C-13-NMR analysis confirmed the presence of benzoguanamine in the modified resins. The addition of benzoguanamine to the MUF resin synthesis significantly improved the flexibility of agglomerated cork panels bound with modified resins. The minimum mandrel diameter on which the panels could be bent by 180 without failure decreased from 18 mm to 12 mm diameter, while the remaining key properties of the panels were maintained (tensile strength and boiling water resistance). The formaldehyde content of the panels (determined according to EN120) corresponds to E1 class.