Carbon-Al2O3-Ag composite molecular sieve membranes for gas separation

• Tipo: Artigo em Revista Científica Internacional
• Data: 2012

Autores

Miguel Teixeira (Autor) FEUP; Marta Campo (Autor) FEUP; Tanaka, D.A. (Autor) FEUP; Tanco, M.A. (Autor) FEUP; Magen C. (Autor) Outra; Mendes, A. (Autor) FEUP

Revista

Título: Chemical Engineering Research and Design

Vol. 90 Nº 12

Páginas: 2338-2345

ISSN: 0263-8762

Editora: Institute of Chemical Engineers

Indexação

ISI Web of Knowledge - 20 Citações

ISI Web of Science

Scopus - 31 Citações

Classificação Científica

FOS: Ciências da engenharia e tecnologias > Engenharia química

Projetos Associados

POCI/EQU/59345/2004 - Desenvolvimento dum Reactor de Membrana Catalítica Cerâmica com Transportadores Fixos para a Separação e Oxidação do Monóxido de Carbono a Dióxido de Carbono

POCI/EQU/59344/2004 - Desenvolvimento duma Membrana e Reactor de Membrana Catalítica Cerâmicos com Transportadores Fixos para a Separação/Purificação de Olefinas

Outras Informações

ID Authenticus: P-002-2JH

DOI: 10.1016/j.cherd.2012.05.016

Abstract (EN): Phenolic resins loaded with two different inorganic fillers (boehmite (gamma-AlO(OH)) and silver (Ag)) were used to prepare composite carbon membranes. Polymer solutions containing gamma-AlO(OH) and AgNO3 were prepared and the effect of Ag on the transport properties of the composite membrane was evaluated. The polymer solutions were coated on alpha-Al2O3 tubes and carbonized in a single dipping-drying-pyrolysis step. After pyrolysis at 550 degrees C, gamma-AlO(OH) yielded gamma-Al2O3, and Ag agglomerated forming spherical nanoparticles of 30 nm in diameter. Ag loading enhanced the carbon membrane performance for several gas pairs of interest, especially for C3H6/C3H8 separation, where the C3H6/C3H8 permselectivity increased from a maximum of 15 to 38. (c) 2012 The Institution of Chemical Engineers. Published by Elsevier B.V. All rights reserved.