Austempered ductile iron with tempered martensite

• Tipo: Artigo em Revista Científica Internacional
• Data: 2002

Autores

H. Santos (Autor) Outra; A. Duarte (Autor) Outra; Jorge Seabra (Autor) FEUP

Revista

Título: International Journal of Cast Metals Research

Vol. 15 Nº 2

Páginas: 117-124

ISSN: 1364-0461

Editora: Taylor & Francis

Indexação

ISI Web of Knowledge - 6 Citações

Scopus - 10 Citações

Classificação Científica

FOS: Ciências da engenharia e tecnologias > Engenharia dos materiais

Outras Informações

ID Authenticus: P-000-RC1

DOI: 10.1080/13640461.2002.11819470

Abstract (EN): In order to austemper a CuMn ductile iron, a new approach was adopted, consisting of a two-step isothermal process imposed on the austenitised material. During the first step, martensite forms and austenite is preserved in the martensitic domain; during the second step, martensite is tempered and austenite is transformed into ausferrite. In this way, an ADI with tempered martensite in its microstructure is obtained. The degree of undercooling (relative to Ms temperature) in the first step controls the martensite fraction. The temperature used in the second step controls the intensity of the martensite tempering and the nature of the ausferrite. Tests were performed in a quenching dilatometer to determine the processing conditions of the ductile iron (temperature and duration of each isothermal stage). Tensile and contact fatigue tests were run to evaluate the mechanical properties of the material after heat treatment. The results show that high tensile strength may be obtained for ADI after a two-step treatment at intermediate temperatures in the bainitic domain (340degreesC) with considerable reduction of processing time and increased contact fatigue life.