Electrochemical and surface modifications on N+-ion-implanted 316L stainless steel

• Tipo: Artigo em Revista Científica Internacional
• Data: 1997

Autores

Leitao, E (Autor) Outra; Silva, RA (Autor) Outra; Mário Adolfo Barbosa (Autor) FEUP

Revista

Título: Journal of Materials Science: Materials in Medicine

Vol. 8 Nº 6

Páginas: 365-368

ISSN: 0957-4530

Editora: Springer Nature

Indexação

ISI Web of Knowledge - 32 Citações

Scopus - 34 Citações

Outras Informações

ID Authenticus: P-001-BBF

DOI: 10.1023/a:1018532900458

Abstract (EN): The effect of nitrogen-ion implantation on the electrochemical behaviour of 316L stainless steel in a simulated physiological solution (HBSS-Hank's Balanced Salt Solution) was studied by open-circuit potential versus time and cyclic polarization techniques, with the aim of characterizing the surfaces and choosing the best nitrogen-ion fluence. Three fluences (10(15), 10(16) and 10(17) ions/cm(2)) were used. The 10(16) ions/cm(2) N+ fluence improves the corrosion resistance of the 316L stainless steel.