Residual Stresses Profiles of Cladded Austenitic Stainless Steel Evaluated by X-Ray Diffraction and by Incremental Hole-Drilling Method

• Tipo: Artigo em Livro de Atas de Conferência Internacional
• Data: 2014

Autores

M. J. Marques (Autor) FEUP; Batista, AC (Autor) Outra; Coelho, L (Autor) Outra; Nobre, JP (Autor) Outra; Loureiro, A (Autor) Outra

Ata de Conferência Internacional

Título: INTERNATIONAL CONFERENCE ON RESIDUAL STRESSES 9 (ICRS 9)

Páginas: 464-469

9th International Conference on Residual Stresses (ICRS 9)

Garmisch-Partenkirchen, GERMANY, OCT 07-09, 2012

Indexação

ISI Web of Knowledge - 0 Citações

Scopus - 0 Citações

Outras Informações

ID Authenticus: P-008-FCN

DOI: 10.4028/www.scientific.net/msf.768-769.464

Abstract (EN): The samples studied in this paper were carried out using carbon steel plates, cladded on one of the faces with stainless steel filler metals by submerged arc welding (SAW). After cladding, the samples were submitted to post-weld heat treatments under different conditions and then stainless steel coating surfaces were milled and mechanically polished, as in the industrial application. The residual stress analysis was performed by X-ray diffraction (XRD) and incremental hole-drilling methods (IHD). The residual stress profiles showed different values in-depth in each sample, depending on the heat treatment. The hole-drilling method was applied in several points of each stainless steel sample surface and the results presented similar profiles of evolution. However, compressive stresses increase when the heat treatment temperature rises.