Study of the annealing influence on the mechanical performance of PA12 and PA12 fibre reinforced FFF printed specimens

• Tipo: Artigo em Revista Científica Internacional
• Data: 2020

Autores

Ferreira, I (Autor) Outra; Melo, C (Autor) Outra; Neto, R (Autor) Outra; Machado, M (Autor) Outra; Jorge Lino (Autor) FEUP; Mould, S (Autor) Outra

Revista

Título: Rapid Prototyping Journal

Vol. ahead-of-print

ISSN: 1355-2546

Editora: Emerald

Indexação

ISI Web of Knowledge - 0 Citações

Scopus - 0 Citações

Outras Informações

ID Authenticus: P-00S-X47

DOI: 10.1108/rpj-10-2019-0278

Abstract (EN): Purpose The purpose of this study is to evaluate and compare the mechanical performance of FFF parts when subjected to post processing thermal treatment. Therefore, a study of the annealing treatment influence on the mechanical properties was performed. For this, two different types of Nylon (PA12) were used, FX256 and CF15, being the second a short fibre reinforcement version of the first one. Design/methodology/approach In this study, tensile and flexural properties of specimens produced via FFF were determined after being annealed at temperatures of 135 degrees C, 150 degrees C or 165 degrees C during 3, 6, 12 or 18 h and compared with the non-treated conditions. Differential scanning calorimetry (DSC) was performed to determine the degree of crystallinity. To evaluate the annealing parameters' influence on the mechanical properties, a full factorial design of experiments was developed, followed by an analysis of variance, as well as post hoc comparisons, to determine the most significative intervening factors and their effect on the results. Findings The results indicate that CF15 increased its tensile modulus, strength, flexural modulus and flexural strength around 11%, while FX256 presented similar values for tensile properties, doubling for flexural results. Flexural strain presented an improvement, indicating an increased interlayer behaviour. Concerning to the DSC analysis, an increase in the degree of crystallinity for all the annealed parts. Originality/value Overall, the annealing treatment process cause a significant improvement in the mechanical performance of the material, with the exception of 165 degrees C annealed specimens, in which a decrease of the mechanical properties was observed, resultant of material degradation.