Tuning of magnetocaloric effect in ferromagnetic La-Sr manganites through Er and Eu doping

• Tipo: Artigo em Revista Científica Internacional
• Data: 2006

Autores

Amaral, J. S. (Autor) Outra; Reis, Mário Souza (Autor) Outra; Amaral, V. S. (Autor) Outra; Mendonça, Tânia Melo (Autor) Outra; Araújo, João Pedro (Autor) FCUP; Tavares, Pedro B. (Autor) Outra; Vieira, Joaquim Manuel (Autor) Outra

Revista

Título: ADVANCED MATERIALS FORUM II

Vol. 514-516

Páginas: 299-303

Editora: Trans Tech Publications Ltd

Indexação

ISI Web of Knowledge - 7 Citações

Scopus - 6 Citações

Outras Informações

ID Authenticus: P-004-NVE

DOI: 10.4028/www.scientific.net/msf.514-516.299

Abstract (EN): Colossal magnetoresistive manganites have attracted renewed interest in research due to their potential application as active magnetic materials in magnetic refrigeration tech- niques. For optimal thermal performace, a careful control of the efficiency peak at the Curie temperature (TC) is needed. La0.70Sr0.30MnO3 (LSMO) is an optimally doped ferromagnetic material manganite that presents considerable magnetocaloric effect. However, the operating temperature (TC) of LSMO is near 375 K, which limits it's applicability in room-temperature refrigeration. In light of this, we have studied solid state and sol-gel produced samples of the LSMO system where La is substituted by Er and Eu, and show that the operating temperature can be significantly controlled by substitution to values near room temperature and also that the relative cooling power (RCP) of Er and Eu substituted samples is significantly increased. The regular dependence of TC with the amount of rare-earth substitution and the increase in RCP allow the creation of composites or thermal cascades of chemically similar compounds to produce an active magnetic element with a wide temperature interval of operation (from 260 to 370 K). This work presents relatively cost-efficient materials for application in room-temperature magnetic cooling.