A comparative study of the corrosion behaviour of flexible dry electrodes based on Ti-Cu thin films

• Tipo: Artigo em Revista Científica Internacional
• Data: 2025

Autores

Camarinha, A (Autor) Outra; Lopes, C (Autor) Outra; Ferreira, A (Autor) Outra; Alves, AC (Autor) FEUP; Vaz, F (Autor) Outra

Revista

Título: SURFACES AND INTERFACES

Vol. 58

ISSN: 2468-0230

Editora: Elsevier

Indexação

ISI Web of Knowledge - 0 Citações

Scopus - 0 Citações

Outras Informações

ID Authenticus: P-017-Z0S

DOI: 10.1016/j.surfin.2025.105855

Abstract (EN): This work investigates the surface behaviour of Ti-based dry electrodes subjected to artificial sweat corrosion, aiming to assess their suitability for long-term neuromuscular rehabilitation in e-health applications. Three types of dry electrodes were prepared by PVD magnetron sputtering, depositing titanium (Ti), titanium dopped with copper (TiCu0.34) and Copper (Cu) thin films on flexible polylactic acid (PLA) polymeric substrates. The electrodes were submitted to corrosion resistance testing using electrochemical methods, including open circuit potential (OCP), potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS). The results were analysed attending to the films' chemical composition, crystalline structure, roughness, and morphology. Despite exposure to corrosive environments, Ti and TiCu0.34 electrodes exhibited minimal surface degradation, with no significant differences in corrosion rate (passivation current densities of approximately 8 and 11 x 10(-6) Acm(-2), respectively). Importantly, the electrical resistivity of the Ti-based electrodes remained stable, with post-corrosion values (TiCu0.34: 10 mu Omegam, Ti: 9 mu Omegam) remaining within the pre-corrosion range (< 10.0 Omegam), indicating strong surface integrity. The findings underscore the strong corrosion resistance and consistent electrical performance of TiCu0.34 thin films, making them promising candidates for long-term use in wearable e-health devices.