Gold on oxide-doped alumina supports as catalysts for CO oxidation

• Tipo: Artigo em Revista Científica Internacional
• Data: 2012

Autores

S. A. C. Carabineiro (Autor) FEUP; P.B. Tavares (Autor) Outra; J. L. Figueiredo (Autor) FEUP

Revista

Título: Applied Nanoscience

Vol. 2 Nº 1

Páginas: 35-46

ISSN: 2190-5509

Editora: Springer Nature

Indexação

ISI Web of Science

Scopus

Classificação Científica

FOS: Ciências da engenharia e tecnologias > Engenharia química

CORDIS: Ciências Físicas > Química > Catálise heterogénea

Outras Informações

Abstract (EN): The effect of doping a commercial alumina support with metal oxides of Ce, Co, Cu, Fe, La, Mg, Mn, Ni and Zn was investigated. Doped d-Al2O3 samples were obtained by simple physical mixture (PM) of the alumina with the desired commercial oxide and by traditional impregnation of alumina with precursor salts of the same metals followed by calcination (IC). The metal load (7% wt.) was the same in both cases. Gold (1% wt.) was loaded using a liquid phase reductive deposition method. The obtained materials were characterized by adsorption of N2 at -196C, temperature programmed reduction, X-ray diffraction, energy-dispersive X-ray spectrometry and transmission electron microscopy. Both samples prepared by PM and IC showed a mixture of the d-alumina phase with the respective metal oxide, but the BET surface areas of the IC samples were, in general, higher than those of the PM materials. The particle size of the oxide phases were larger for the PM samples than for the IC materials. Nevertheless, catalytic experiments for CO oxidation showed that PM samples were much more active than IC. That could be explained by the size of gold nanoparticles, well known to be related with catalytic activity, that was lower in samples prepared by PM (7–16 nm) than by IC (11–17 nm). Gold was found to be in the metallic state. The most active samples were aluminas containing Zn and Fe prepared by PM that had the smallest gold nanoparticlessizes (7–13 and 8–12 nm, respectively) and had room temperature activities for CO conversion of 0.62 and 1.34 mol CO h-1 g Au-1, respectively, which are larger than those found in the literature for doped c-alumina samples.