Mechanical characterization of porous glass-reinforced hydroxyapatite ceramics-Bonelike

• Tipo: Artigo em Revista Científica Internacional
• Data: 2003

Autores

Marcelo Henrique Prado da Silva (Autor) Outra; Alexandra Fernandes Lemos (Autor) Outra; José Maria da Fonte Ferreira (Autor) Outra; José Domingos Santos (Autor) FEUP

Revista

Título: Materials Research

Vol. 6 Nº 3

Páginas: 321-325

ISSN: 1516-1439

Editora: Universidade Federal de Sao Carlos

Classificação Científica

FOS: Ciências médicas e da saúde > Biotecnologia médica

Outras Informações

Abstract (EN): In the present study, mechanical properties of porous glass reinforced hydroxyapatite bioceramics were assessed by microhardness, bending and compression tests and fracture toughness determination. Porous discs were produced by a dry method using wax spheres as pore formers. Green bodies were sintered and the final microstructure of the composites consists of hydroxyapatite, alpha and beta tricalcium phosphate (α and β-Ca3 (PO4 )2 )due to the reaction between the glassy phase and the hydroxyapatite matrix. The results of the mechanical tests showed that the glassy phase yielded higher fracture toughness and bending strength when comparing with literature data for single hydroxyapatite. There is a compromise between mechanical properties and the porosity level for bioceramics: for example, according to Weibull statistics for composites with 65% porosity the maximum bending stress level is 0.2 MPa for 100% survival probability whereas this stress level increases to 2.5 MPa for composites with 40%. However, only the 65% porosity composite samples seem to have the complete adequate morphology for bone ingrowth.

Idioma: Inglês

Tipo (Avaliação Docente): Científica

Nº de páginas: 5