Nonlinear electrical transport via grain boundary tunneling in La-deficient compound La0.9Mn0.9Co0.1O3

• Tipo: Artigo em Revista Científica Internacional
• Data: 2010

Autores

De, K (Autor) Outra; Roy, A (Autor) Outra; Silva, CJR (Autor) Outra; Gomes, MJM (Autor) Outra

Revista

Título: Solid State Communications

Vol. 150

Páginas: 1187-1191

ISSN: 0038-1098

Editora: Elsevier

Indexação

ISI Web of Knowledge - 4 Citações

Scopus - 4 Citações

Outras Informações

ID Authenticus: P-003-5HM

DOI: 10.1016/j.ssc.2010.04.016

Abstract (EN): Nonlinear electrical transport properties in La-deficient compound La0.9Mn0.9Co0.1O3 have been investigated as a function of temperature (T) and magnetic field (H). The experiment was carried out through temperature range 20-293 K and in magnetic field up to 5 kOe. The nonlinear electrical transport was studied in low temperature region below the paramagnetic to ferromagnetic transition temperature (T-C) at 195 K. The analysis of current-voltage (I-V) characteristic shows that the transport through grain boundary (GB) is dominated by multi-step inelastic tunneling in low temperature. This transport is also effected by magnetic field. Zero bias conductance [G(0) = (dI/dV)(V=0)] is enhanced in the presence of magnetic field. The electrical transport properties have been interpreted in terms of tunneling through the GB region where substitution of Mn by Co introduces more disorder in GB.

Idioma: Inglês

Tipo (Avaliação Docente): Científica

Nº de páginas: 5