Mechanical Characterization of Flexible Adhesives

• Tipo: Artigo em Revista Científica Internacional
• Data: 2009

Autores

Mariana D Banea (Autor) FEUP; Lucas F M da Silva (Autor) FEUP

Revista

Título: Journal of Adhesion

Vol. 85

Páginas: 261-285

ISSN: 0021-8464

Editora: Taylor & Francis

Indexação

ISI Web of Knowledge - 69 Citações

Scopus - 103 Citações

Classificação Científica

FOS: Ciências da engenharia e tecnologias > Engenharia química

Outras Informações

ID Authenticus: P-003-QS7

DOI: 10.1080/00218460902881808

Abstract (EN): In this paper, the performances of two different adhesive typesa polyurethane and a high temperature thixotropic adhesive sealant, room temperature vulcanizing (RTV) silicone rubberwere studied through adhesive joint tests. The standard Thick Adherend Shear Test (TAST) was performed in order to measure the shear properties of the adhesives. Single lap joints (SLJs) were fabricated and tested to assess the adhesive performance in a joint. The influence of temperature on the lap shear strength of the adhesives was investigated. It is shown that the lap shear strength of both adhesives is affected by variation of temperature. The effect of bondline thickness and overlap length on the lap shear strength of the adhesives was studied. The reduction of failure load with increasing the bondline thickness is a very common situation when dealing with structural adhesives. For the low strength flexible adhesive Sikaflex 552 the failure load as well as the overall stiffness of the SLJs decreases as the bondline gets thicker, whereas for AS1805 RTV adhesive the failure loads increase as the bondline gets thicker. Also, in contrast to joints with brittle adhesives, the failure loads of joints with flexible adhesives increase almost proportionally with increasing overlap length. Fatigue tests were also performed and show a low variability in the results.

Idioma: Inglês

Tipo (Avaliação Docente): Científica

Nº de páginas: 25