Displacement rate effect in the fracture toughness of glass fiber reinforced polyurethane

• Tipo: Artigo em Revista Científica Internacional
• Data: 2020

Autores

Reis, JML (Autor) Outra; Machado, JJM (Autor) FEUP; Marques, EAS (Autor) FEUP; Ricardo Carbas (Autor) FEUP; da Silva, LFM (Autor) FEUP

Revista

Título: Journal of Composite Materials

Vol. 54 Nº 22

Páginas: 3047-3054

ISSN: 0021-9983

Editora: SAGE

Indexação

ISI Web of Knowledge - 3 Citações

Scopus - 3 Citações

Outras Informações

ID Authenticus: P-00R-WTP

DOI: 10.1177/0021998320908300

Abstract (EN): Composite structures currently used in the oil industry must meet strict requirements for design and safety reasons. They need to maintain strength under varied displacement rates throughout its lifetime. It is therefore critical to fully understand the fracture behavior of such composites. This work presents experimental results regarding the influence of a range of displacement rates on the fracture energy in mode I, G(Ic), of glass fiber reinforced polyurethane used in the oil industry to repair and reinforce pipelines with corrosion damage. To determine G(I)(c) as a function of displacement rate, double cantilever beam specimens were tested, with displacement rates of 2, 20 and 200 mm/min with different thicknesses. A complementary numerical study was performed with the aim of predicting strength using the measured values. This work has demonstrated a significant influence of the strain rate and composite thickness on G(IC) of the composite materials, with higher rates and thicker specimens causing an increase in the G(IC) values.