Abstract (EN):
Ion Beam sputtered Co80Fe20(t)/Al2O3(30 Angstrom) multilayers were obtained. The Co80Fe20 layers become discontinuous for nominal thickness t less than or equal to 18 Angstrom. Tunnel magnetoresistance was measured in CIP and CPP geometries, reaching up to 6.5% at room temperature and 11% at 15 K, for as-deposited films in CIP geometry. The temperature dependence of MR was found quite different for the two geometries: fairly strong in the CIP case and almost absent in the CPP geometry. A model is proposed to explain these large differences in behavior.