Investigation of Stereometric and Fractal Patterns of Spin-Coated LuMnO3 Thin Films

• Tipo: Artigo em Revista Científica Internacional
• Data: 2021

Autores

Marques, IHG (Autor) Outra; Matos, RS (Autor) Outra; Romaguera Barcelay, Y (Autor) Outra; Talu, S (Autor) Outra; Agostinho Moreira, JA (Autor) FCUP; Almeida, A (Autor) FCUP; de Cruz, JP (Autor) Outra; da Fonseca, HD (Autor) Outra

Revista

Título: Advances in Materials Science and Engineering

Vol. 2021

Páginas: 1-11

ISSN: 1687-8434

Editora: Hindawi

Indexação

ISI Web of Knowledge - 5 Citações

Outras Informações

ID Authenticus: P-00T-Z2F

DOI: 10.1155/2021/9912247

Abstract (EN): In this paper, we have performed qualitative and quantitative analysis of LuMnO3 thin films surfaces, deposited by spin coating over Pt(111)/TiO2/SiO2/Si substrates, to evaluate their spatial patterns as a function of the film's sintering temperature. Atomic force microscopy was employed to obtain topographic maps that were extensively analyzed via image processing techniques and mathematical tools. 3D (three-dimensional) topographical images revealed that films sintered at 650 degrees C and 750 degrees C presented the formation of smoother surfaces, while the film sintered at 850 degrees C displayed a rougher surface with a root mean square roughness of similar to 2.5 nm. On the other direction, the height distribution of the surface for all films has similar asymmetries and shape, although the film sintered using the highest temperature showed the lower density of rough peaks and a sharper peak shape. The advanced fractal parameters revealed that the film sintered at 850 degrees C is dominated by low spatial frequencies, showing less spatial complexity, higher microtexture homogeneity, and uniform height distribution. These results suggest that the combination of stereometric and fractal parameters can be especially useful for identification of unique topographic spatial patterns in LuMnO3 thin films, helping in their implementation in technological applications, such as photovoltaic solar cells and information magnetic date storage and spintronic devices.