Highly electroactive N-Fe hydrothermal carbons and carbon nanotubes for the oxygen reduction reaction

• Tipo: Artigo em Revista Científica Internacional
• Data: 2020

Autores

Rafael Morais (Autor) FEUP; Rey Raap, N (Autor) Outra; Figueiredo, JL (Autor) Outra; Manuel Fernando R Pereira (Autor) FEUP

Revista

Título: Journal of Energy Chemistry

Vol. 50

Páginas: 260-270

ISSN: 2095-4956

Editora: Elsevier

Indexação

ISI Web of Knowledge - 0 Citações

Scopus - 3 Citações

Projetos Associados

LA LSRE-LCM - Financiamento Plurianual 2020-2023 para a Unidade LA LSRE-LCM Laboratório de Processos de Separação e Reacção - Laboratório de Catálise e Materiais

AIProcMat@N2020 - Advanced Industrial Processes and Materials for a Sustainable North Region of Portugal2020

UnirCell - Project UniRCell - Unitised Regenerative Fuel Cell for Efficient Renewable Energy Supply: from Materials to Device

Outras Informações

ID Authenticus: P-00S-07K

DOI: 10.1016/j.jechem.2020.03.039

Abstract (EN): Glucose-derived carbons were prepared by hydrothermal carbonization of glucose followed by carbonization or activation to obtain carbon materials with different microporosities. These microporous carbons and carbon nanotubes (CNTs) were functionalized with melamine and/or iron(II) phthalocyanine (FePc) following three different methodologies: (i) Functionalization with melamine via thermal treatment, (ii) incorporation of the lowest amount of FePc reported in the literature via incipient wetness impregnation followed by thermal treatment and (iii) functionalization with melamine followed by FePc incorporation. The chemical and textural characterization of the prepared materials and their electrochemical assessment allowed to understand the role of microporosity in the incorporation of FePc and its effect on the oxygen reduction reaction (ORR). It was observed that FePc was preferentially incorporated inside the porous structure, especially in samples with more developed microporosity. However, functionalization with melamine modified the textural properties and the surface chemistry, favoring the incorporation of FePc on the surface. Regarding the electrochemical performance, the presence of FePc greatly enhanced the electroactivity of the microporous catalysts. An onset potential of 0.88 V and a four-electron pathway were obtained for glucose-derived carbons, whereas the limiting current densities and kinetic current densities rose by 126% and 222%, respectively, in comparison to the base sample. Not with standing, the highest electrochemical activity was observed for the sample prepared with CNTs, due to the synergy between the active metal centers and their highly graphitic carbon structure. The electrochemical parameters of CNTFePc surpass the commercial Pt/C. The half-wave potential is 40 mV higher, the limiting current density increases by 17%, and a negligible production of by-products (< 1%) was observed.