Co-precipitation of a Ni-Zn ferrite precursor powder: Effects of heat treatment conditions and deagglomeration on the structure and magnetic properties

• Tipo: Artigo em Revista Científica Internacional
• Data: 2012

Autores

Olhero, SM (Autor) Outra; Soma, D (Autor) Outra; Amaral, V. S. (Autor) Outra; Button, TW (Autor) Outra; Jorge Lino (Autor) FEUP; Ferreira, JMF (Autor) Outra

Revista

Título: Journal of the European Ceramic Society

Vol. 32

Páginas: 2469-2476

ISSN: 0955-2219

Editora: Elsevier

Indexação

ISI Web of Knowledge - 22 Citações

Scopus - 30 Citações

Outras Informações

ID Authenticus: P-002-7SZ

DOI: 10.1016/j.jeurceramsoc.2012.03.017

Abstract (EN): A Ni-Zn ferrite precursor powder was synthesized by co-precipitation upon adding ammonia to an aqueous solution of the precursor iron, nickel, and zinc nitrate salts. The powder was calcined at a range of temperatures (200-1200 degrees C) and the crystalline phase evolution was assessed by X-ray diffraction coupled with Rietveld refinement. Intermediate phases (NiFe2O4 and Fe2O3) with increasing crystallinity coexisted in the system up to 1000 degrees C. The required Ni0.8Zn0.2Fe2O4 phase could only be attained at 1200 degrees C. The magnetic properties measured using a vibrating sample magnetometer revealed high magnetization saturation level (similar to 59 emu/gm) above 400 degrees C. The coercivity showed a steady decrease with increasing heat treatment temperature, leading to a change from a hard to soft magnetic state. The BET specific surface area and the SEM morphology were found to be dependent on calcination temperature, atmosphere (air or N-2) and on the milling procedure.

Idioma: Inglês

Tipo (Avaliação Docente): Científica

Nº de páginas: 8