Preparation and properties of new flame retardant unsaturated polyester nanocomposites based on layered double hydroxides

• Tipo: Artigo em Revista Científica Internacional
• Data: 2009

Autores

Pereira, CMC (Autor) Outra; Herrero, M (Autor) Outra; Labajos, FM (Autor) Outra; António Torres Marques (Autor) FEUP; Rives, V (Autor) Outra

Revista

Título: Polymer Degradation and Stability

Vol. 94

Páginas: 939-946

ISSN: 0141-3910

Editora: Elsevier

Indexação

ISI Web of Knowledge - 80 Citações

Scopus - 46 Citações

Outras Informações

ID Authenticus: P-003-JXP

DOI: 10.1016/j.polymdegradstab.2009.03.009

Abstract (EN): The preparation of new layered double hydroxides/unsaturated polyester (LDH/UP) nanocomposites was performed and the effect of LDH on the resin properties was studied. Two different organo-LDHs have been prepared, adipate-LDH (A-LDH) and 2-methyl-2-propene-1-sulfonate-LDH (S-LDH); in order to evaluate the influence of these nanofillers, samples with two different concentrations were dispersed in the matrix. The physical, thermal, mechanical and fire reaction properties of nanocomposites were studied. Intercalated layered structures were observed for the different organo-LDH loadings (1 and 5 wt%). Mechanical properties studied Under flexural tests show that incorporation of organo-LDH in the resin reduces the flexural strength of polyester resin while the flexural modulus is unchanged for the S-LDH/UP composites and increased with 1 wt% of A-LDH. Adding 1 wt% of A-LDH to the resin produces an important reduction on the flexural strength, but an increase of the flexural modulus. The study of fire using cone calorimeter, suggested a significant reduction in the UP flammability, by reaction properties, 46 and 32%, by incorporating 1 wt% of A-LDH and 5 wt% S-LDH, respectively. Mass loss curves show enhanced char formation with the different loads tested while the amount of evolved smoke remains quite unchanged.