Characterisation of unidirectional Carbon-Epoxy IM7-8552 in longitudinal compression under high strain rates

• Tipo: Artigo em Livro de Atas de Conferência Internacional
• Data: 2009

Autores

Koerber, H (Autor) Outra; Camanho, PP (Autor) FEUP

Ata de Conferência Internacional

Título: DYMAT 2009: 9TH INTERNATIONAL CONFERENCE ON THE MECHANICAL AND PHYSICAL BEHAVIOUR OF MATERIALS UNDER DYNAMIC LOADING, VOL 1

Páginas: 185-191

9th International Conference on Mechanical and Physical Behaviour of Materials under Dynamic Loading

Brussels, BELGIUM, SEP 07-11, 2009

Indexação

ISI Web of Knowledge - 2 Citações

Outras Informações

ID Authenticus: P-003-PQN

DOI: 10.1051/dymat/2009025

Abstract (EN): A self-aligning Dynamic Compression Fixture, which can be used with a conventional Split-Hopkinson Pressure Bar, was developed to characterise the advanced composite carbon/epoxy material system IM7-8552 in longitudinal compression under high strain rates. The development of the dynamic experiment was supported by Finite Element Analysis, using a simple axi-symmetric elastic model of the dynamic test setup. Due to the quasi-brittle material behaviour in the longitudinal direction, a triangular shaped pulse is used, which creates a near constant strain rate while also ensuring dynamic equilibrium throughout the test. Tungsten-carbide inserts were used at the bar-specimen interfaces to prevent indentation of the bar ends due to the high strength specimen used. The results from the Split-Hopkinson Pressure Bar experiment, at a strain rate of approx. 100 s(-1), were compared with results from quasi-static tests using the same test setup. Analysing the first test results it is likely that the longitudinal compressive chord modulus of elasticity is not strain rate sensitive while an increase was found for the longitudinal compressive strength.