Characterization and application of composite membranes in DMFC

• Tipo: Artigo em Revista Científica Internacional
• Data: 2005

Autores

silva, vs (Autor) Outra; ruffmann, b (Autor) Outra; vetter, s (Autor) Outra; mendes, a (Autor) FEUP; madeira, lm (Autor) FEUP; nunes, sp (Autor) Outra

Revista

Título: Catalysis Today

Vol. 104

Páginas: 205-212

ISSN: 0920-5861

Editora: Elsevier

Indexação

ISI Web of Knowledge - 69 Citações

Scopus - 81 Citações

Outras Informações

ID Authenticus: P-000-2SJ

DOI: 10.1016/j.cattod.2005.03.051

Abstract (EN): The present work focuses on the characterization of membranes for direct methanol fuel cells (DMFC), prepared using composites of sulfonated poly(ether ether ketone) (sPEEK, with sulfonation degree, SD, of 42 and 68%) as polymer matrix. This polymer was inorganically modified incorporating different amounts of zirconium phosphate (ZrPh) pretreated with n-propylamine and polybenzimidazole (PBI). The investigated properties were: proton conductivity, water and aqueous methanol swelling, permeability coefficients for DMFC species and morphology. DMFC tests were performed at 110 degrees C with relative humidity (r.h.) in the cathode feed of 100 and 138%. The results obtained show that the inorganic modification of the polymer decreases the proton conductivity, water and aqueous methanol swelling and permeability towards DMFC species. In terms of morphology, it was found that the applied procedure enabled the preparation of membranes with good compatibility between inorganic and organic components. In terms of the DMFC tests of the composite membranes, working with the cathode feed at 100% r.h., the unmodified sPEEK membrane with SD = 42% proved to have the best performance, although with higher methanol crossover. In contrast, for r.h. of 138%, the best performance was achieved by the sPEEK composite membrane with SD = 68 and 20.0 wt.% of ZrPh and 11.2 wt.% of PBI.