Low Temperature Deposition of Ferromagnetic Ni-Mn-Ga Thin Films From Two Different Targets via rf Magnetron Sputtering

• Tipo: Artigo em Revista Científica Internacional
• Data: 2010

Autores

Lourenço, AC (Autor) Outra; Figueiras, F (Autor) Outra; Das, S (Autor) Outra; Amaral, JS (Autor) Outra; G.N. Kakazei (Autor) REIT; Karpinsky, DV (Autor) Outra; Soares, N (Autor) Outra; Peres, M (Autor) Outra; Pereira, MJ (Autor) Outra; Tavares, PB (Autor) Outra; Sobolev, N (Autor) Outra; Amaral, V (Autor) Outra; Santos, NM (Autor) Outra; Kholkin, AL (Autor) Outra

Revista

A Revista está pendente de validação pelos Serviços Administrativos.

Título: MRS Proceedings

Vol. 1250

ISSN: 0272-9172

Outras Informações

ID Authenticus: P-00V-5EJ

DOI: 10.1557/proc-1250-g08-02

Abstract (EN): <jats:title>Abstract</jats:title><jats:p>Low temperature (400°C) deposition of ferromagnetic Ni-Mn-Ga thin films is successfully performed via rf magnetron sputtering technique using co-deposition of two targets Ni<jats:sub>50</jats:sub>Mn<jats:sub>50</jats:sub> and Ni<jats:sub>50</jats:sub>Ga<jats:sub>50</jats:sub> on sapphire (0001) and Si (100) substrates. The films are in part amorphous with significant degree of crystallinity. The obtained crystallographic structure is shown to be substrate-dependent. Films on both substrates are ferromagnetic at room temperature (Curie temperature ~ 332.5K) with well-defined hysteresis loops, low coercivity (~ 100 Oe) and a saturation magnetization of ~ 200 emu/cc. At low temperature (5 K), both films show increased magnetization value with wider hysteresis loops having higher coercivity and remanent magnetization. The process is therefore effective in achieving the appropriate thermodynamic conditions to deposit thin films of the Ni-Mn-Ga austenitic phase (highly magnetic at room temperature) at relatively low substrate temperature without the need for post-deposition annealing or further thermal treatment, which is prerequisite for the device fabrication.</jats:p>