Effects of cyclic ageing on the tensile properties and diffusion coefficients of an epoxy-based adhesive

• Tipo: Artigo em Revista Científica Internacional
• Data: 2021

Autores

da Costa, JA (Autor) Outra; Akhavan Safar, A (Autor) Outra; Marques, EAS (Autor) FEUP; Ricardo Carbas (Autor) FEUP; da Silva, LFM (Autor) FEUP

Revista

Título: Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications

Vol. 235

Páginas: 1451-1460

ISSN: 1464-4207

Editora: SAGE

Indexação

ISI Web of Knowledge - 1 Citação

Scopus - 2 Citações

Outras Informações

ID Authenticus: P-00T-HQ1

DOI: 10.1177/1464420721994871

Abstract (EN): In real practice, adhesively bonded structures are usually exposed to cyclic environmental conditions. However, cyclic ageing processes are relatively unexplored. The aim of this study is to consider the effect of cyclic ageing on the rate of water uptake and the drying process in an epoxy-based adhesive. Fick's law was considered to estimate the water diffusion coefficients for the ageing and the drying steps at different cycles. Different cyclic ageing times have been considered in the ageing procedure. Dogbone shape specimens were also manufactured and subjected to cyclic aging to investigate the tensile properties of the tested adhesive as a function of aging cycles. The gravimetric results showed that the rate of water uptake and drying is mainly a function of the level of water uptake of the first ageing cycle. Tensile test results showed that the maximum water content increases with each subsequent ageing cycle. It was also found that the Young's modulus and the tensile strength of the adhesive decreased significantly after the initial ageing cycle, but all subsequent ageing cycles have considerably less influence on the mechanical properties of the adhesive.