Interlaminar to intralaminar mode I and II crack bifurcation due to aligned carbon nanotube reinforcement of aerospace-grade advanced composites

• Tipo: Artigo em Revista Científica Internacional
• Data: 2020

Autores

Ni, XC (Autor) Outra; Furtado, C (Autor) FEUP; Fritz, NK (Autor) Outra; Kopp, R (Autor) Outra; Camanho, PP (Autor) FEUP; Wardle, BL (Autor) Outra

Revista

Título: Composites Science and Technology

Vol. 190

ISSN: 0266-3538

Editora: Elsevier

Indexação

ISI Web of Knowledge - 37 Citações

Scopus - 48 Citações

Outras Informações

ID Authenticus: P-00R-QG4

DOI: 10.1016/j.compscitech.2020.108014

Abstract (EN): Aerospace-grade unidirectional carbon microfiber reinforced epoxy prepreg composite laminates were reinforced in the relatively weak interlaminar regions with high densities (>10 billion nanofibers per cm(2)) of uniformlydistributed vertically aligned carbon nanotubes (A-CNTs), creating a hierarchical architecture termed "nano stitch". Such nanostitched laminates have been shown to increase laminate in-plane and interlaminar shear strengths. Here, the Mode I and Mode II fracture behavior and associated toughening mechanisms are investigated experimentally by performing double cantilever beam and end-notched flexure tests, respectively, of unidirectional 0 degrees laminates following the ASTM Standards. Investigation of the crack surfaces via microscopy and micro-computed tomography (CT) show that in both Mode I and II, the interlaminar crack bifurcates into the intralaminar region from the interlaminar precrack, and then propagates within the intralaminar region parallel to the nanostitched interlaminar region as an "intralaminar delamination" in steady state. This before unobserved phenomenon is attributed to the A-CNTs adding interlaminar toughness to a level that causes the interlaminar crack to bifurcate into the less tough intralaminar region. Microscopy and mu CT analyses reveal that the A-CNTs do not increase the interlaminar thickness, and drive the crack into the intralaminar region within 1-2 nun of crack initiation in both Mode I and II, with the distance of the "intralaminar delamination- crack from the interlaminar region (at the laminate centerline) being greater in Mode II than in Mode I ((similar to)30 mu m vs. (similar to)15 pm, respectively). Finite element simulation of the crack bifurcation in Mode I predicts a minimum of 10% increase in interlaminar toughness due to the A-CNTs to propagate the crack in the intralaminar region in steady state, as observed experimentally. This unique crack behavior in advanced composites provides new insights into the magnitude and effects of reinforcement induced by A-CNTs that influence the macroscopic fracture and failure behavior of laminates, and suggests new opportunities for toughening laminates.