Effect on the electrical and morphological properties of Bi incorporation into ZnO:Ga and ZnO:Al thin films deposited by confocal magnetron sputtering

• Tipo: Artigo em Revista Científica Internacional
• Data: 2018

Autores

F. C. Correia (Autor) Outra; P. B. Salvador (Autor) Outra; J. M. Ribeiro (Autor) Outra; Adélio Mendes (Autor) FEUP; C. J. Tavares (Autor) Outra

Revista

Título: Vacuum

Vol. 152

Páginas: 252-260

ISSN: 0042-207X

Editora: Elsevier

Indexação

ISI Web of Knowledge - 4 Citações

ISI Web of Science

Scopus - 9 Citações

INSPEC

Projetos Associados

WINPSC - Novos avanços tecnológicos para a terceira geração de células solares sensibilizadas com perovskita

Outras Informações

ID Authenticus: P-00N-SR6

DOI: 10.1016/j.vacuum.2018.03.033

Abstract (EN): This paper reports the effect on the electrical and morphological properties of co-doping ZnO thin films with Bi and Al or Ga. To do so, a confocal sputtering geometry was used with a Bi target and two intrinsically doped ZnO:Ga and ZnO:Al targets. By depositing at an intentional heating of 200 C and applying a post-deposition thermal treatment at 350 degrees C and 300 degrees C, for ZnO:Ga,Bi and ZnO:AI,Bi, respectively, electrical resistivity values of 1.3 x 10(-3) Omega cm and 4.8 x 10(-4) Omega cm were achieved, with an optical transmittance above 80%. The X-ray diffraction data shows that all doped ZnO films have a wurtzite hexagonal structure with preferential crystal growth perpendicular to the (002) plane. The Seebeck coefficient was measured for the ZnO:AI,Bi films, where a maximum value of -48 mu V K-1 was registered. The optimized electrical properties were correlated with the preferential crystalline texture along [001] and the corresponding current density applied to the Bi dopant target, J(Bi), ZnO:AI,Bi films present out-of-plane compression stress, which concomitantly increases with J(Bi), due to higher compact volume of unit cell with lower lattice parameter c when compared with the undoped ZnO. By controlling the incorporation of Bi, the deposition temperature and the post-deposition thermal treatment temperature, improvements on the thermoelectric power factor of ZnO:Ga and ZnO:Al thin films can be achieved.