Effect of acids and alkalis on the resistance of a polypropylene geotextile against thermo-oxidation

• Tipo: Artigo em Revista Científica Internacional
• Data: 2019

Autores

Maria de Lurdes Lopes (Autor) FEUP; José Ricardo Carneiro (Autor) FEUP; Paulo Joaquim Almeida (Autor) FCUP

Revista

Título: Journal of Construction Research

Páginas: 1-8

ISSN: 1609-9451

Editora: World Scientific Publishing Co.

Classificação Científica

CORDIS: Ciências Tecnológicas

FOS: Ciências da engenharia e tecnologias

Projetos Associados

GeoSynergism - Avaliação de Efeitos Sinérgicos na Degradação de Geossintéticos (GeoSinergismo)

Outras Informações

ID Authenticus: P-00T-JB4

DOI: 10.30564/jcr.v1i1.152

Abstract (EN): <jats:p>The long-term behaviour of geosynthetics is one of the most important topics in the research about these materials. This work studies the effect of some liquids (water, sulphuric acid 0.1 mol.L-1 and sodium hydroxide 0.1 mol.L-1) in the resistance of a polypropylene geotextile against thermo-oxidation. For that purpose, the geotextile was (1) exposed in isolation to the liquids (immersion tests) and to thermo-oxidation (oven-ageing tests) and (2) exposed consecutively to both degradation tests (combined effect). The damage suffered by the geotextile in the degradation tests was evaluated by monitoring changes in its tensile behaviour. Based on the changes occurred in tensile strength, reduction factors were determined. The reduction factors obtained in the successive exposures to liquids and thermo-oxidation were compared with the reduction factors determined by the traditional methodology for the combined effect of those agents. The results, among other findings, showed the existence of an effect of sulphuric acid 0.1 mol.L-1 in the resistance of the geotextile against thermo-oxidation. Indeed, the successive exposure to sulphuric acid 0.1 mol.L-1 and thermo-oxidation (two agents that individually did not cause relevant damage) led to some degradation. Due to the interaction occurred between the degradation agents, the traditional methodology was unable to predict correctly (by underestimating) the reduction factor for the combined effect of sulphuric acid 0.1 mol.L-1 and thermo-oxidation.</jats:p>