Fracture toughness of the interface between Ni-Cr/ceramic, alumina/ceramic and zirconia/ceramic systems

Title
Fracture toughness of the interface between Ni-Cr/ceramic, alumina/ceramic and zirconia/ceramic systems
Type
Article in International Scientific Journal
Year
2016
Authors
Porto, CPS
(Author)
Other
The person does not belong to the institution. The person does not belong to the institution. The person does not belong to the institution. Without AUTHENTICUS Without ORCID
Parente, MPL
(Author)
FEUP
View Personal Page You do not have permissions to view the institutional email. Search for Participant Publications View Authenticus page View ORCID page
Renato Natal Jorge
(Author)
FEUP
View Personal Page You do not have permissions to view the institutional email. Search for Participant Publications View Authenticus page View ORCID page
Pereira, LC
(Author)
Other
The person does not belong to the institution. The person does not belong to the institution. The person does not belong to the institution. Without AUTHENTICUS Without ORCID
Griza, S
(Author)
Other
The person does not belong to the institution. The person does not belong to the institution. The person does not belong to the institution. Without AUTHENTICUS Without ORCID
Journal
Vol. 39
Pages: 817-829
ISSN: 8756-758X
Publisher: Wiley-Blackwell
Other information
Authenticus ID: P-00K-HTK
Abstract (EN): Few studies have focused on the interface fracture performance of bi-layered structures, which have an important role in dental restorations, using ceramic materials. The purpose of this study is to evaluate the fracture mechanics performance of the Ni-Cr/ceramic, alumina/ceramic and zirconia/ceramic interfaces by investigating the propagation of an interfacial crack under a wide range of mode mixities. The effect of the mechanical properties of the base materials and the interface, on the crack initiation and crack path, will also be studied. The finite element method (FEM) was used to calibrate the production of the experimental specimens, allowing to obtain the minimum dimensions and amounts of material needed to correctly characterize the fracture event. The specimens were tested until failure using a three-point bending test machine. The interface fracture parameters were obtained using the FEM. For all specimens, the cracks propagated into the ceramic. The results suggest that, in Ni-Cr/ceramic, alumina/ceramic and zirconia/ceramic bi-layered structures, the ceramic is weaker than the interface, which can be used to explain the clinical phenomenon that the ceramic chipping rate is larger than interface delamination rate. Consequently, a ceramic material with a larger fracture toughness is needed to decrease the failure rate of ceramic restorations.
Language: English
Type (Professor's evaluation): Scientific
No. of pages: 13
Documents
We could not find any documents associated to the publication.
Related Publications

Of the same authors

Fracture toughness in interface systems Ni-Cr/ceramic, alumina/ceramic and zirconia/ceramic (2014)
Article in International Conference Proceedings Book
Porto, CPS; Parente, MPL; Renato Natal Jorge; Pereira, LC; Griza, S

Of the same journal

Guest editorial: Special issue-New trends in fatigue and fracture (NT2F18) (2019)
Another Publication in an International Scientific Journal
Luís Reis; Manuel de Freitas; Paulo Tavares de Castro
Guest editorial: Advanced design and fatigue assessment of structural components (2019)
Another Publication in an International Scientific Journal
Correia, JAFO; Berto, F; Ayatollahi, M; Marsavina, L; Kotousov, A; Sedmak, A
Current fatigue and fracture research in Portugal (2004)
Another Publication in an International Scientific Journal
Paulo Tavares de Castro
Validation of procedures for fatigue life assessment of a steel pressure vessel (2004)
Article in International Scientific Journal
Abílio Pinho de Jesus; A. S. Ribeiro; António Fernandes
The role of loading mode on the property degradation of adhesives at high temperatures (2023)
Article in International Scientific Journal
Lopes, FVBD; Akhavan-Safar, A; Ricardo Carbas; Marques, EAS; Goyal, R; Jennings, J; da Silva, LFM

See all (25)

Recommend this page Top
Copyright 1996-2025 © Faculdade de Direito da Universidade do Porto  I Terms and Conditions  I Acessibility  I Index A-Z
Page created on: 2025-07-24 at 11:14:59 | Privacy Policy | Personal Data Protection Policy | Whistleblowing