A novel generation of hybrid photochromic vinylidene-naphthofuran silica nanoparticles through fine-tuning of surface chemistry

• Type: Article in International Scientific Journal
• Date: 2017

Authors

Pinto, TV (Author) Other; Sousa, CM (Author) Other; Sousa, CAD (Author) Other; Aboelhassan, MM (Author) Other; Peixoto, AF (Author) FCUP; Clara Pereira (Author) FCUP; Coelho, PJ (Author) Other; Cristina Freire (Author) FCUP

Journal

Title: Dalton Transactions

Vol. 46

Pages: 9076-9087

ISSN: 1477-9226

Publisher: Royal Society of Chemistry

Indexing

ISI Web of Knowledge - 9 Citations

Scopus - 9 Citations

Other information

Authenticus ID: P-00N-1HA

DOI: 10.1039/c7dt01376k

Abstract (EN): Novel photochromic 1-vinylidene-naphtho[2,1-b]furan derivatives (VNF-1 and VNF-2) were successfully anchored onto silica nanoparticles (SiO2 NPs) through direct adsorption (SiO2@VNF-1) and covalent postgrafting (SiO2@VNF-2). SiO2 NPs with different sizes (15 +/- 3 and 123 +/- 7 nm) and surface chemistry (pH(pzc) in the range of 5-9) were used, offering a wide range of possibilities to fabricate tailor-made photochromic materials. The characterization of VNF-based SiO2 NPs confirmed the efficient VNF immobilization and the integrity of both organic and inorganic components. The photochromic behavior of these new nanoparticles indicates that silica surface acidity and the type of VNF immobilization strategy (adsorption vs. covalent grafting) were crucial factors for the occurrence of photochromism in the VNF-based SiO2 NPs. Upon UV (lambda = 365 nm) or sunlight exposure for 1 min, only the SiO2@VNF-1 nanomaterials prepared by direct VNF adsorption onto SiO2 NPs with pH(pzc) approximate to 6.0 showed direct and reversible photochromic properties, developing fast (in seconds) and intense salmon and violet coloration, with high values of total color difference (Delta E-ab* = 10.7 +/- 24.3) and optical densities (Delta OD = 0.14-0.25). In contrast, all nanomaterials prepared by covalent grafting of VNF-2 onto SiO2 NPs (SiO2@VNF-2) did not exhibit photochromism. In the case of the photochromic SiO2@VNF-1 NPs, the decoloration process followed a bi-exponential decay with fast rate constants (k(1) = 1.6 x 10(-1) 1.6 min(-1) and k(2) = 9.1 x 10(-3) 1.3 x 10(-1) min(-1)), which were responsible for the loss of coloration in less than 10 min. Furthermore, they presented very good resistance to fatigue, showing reversibility between the colored/uncolored states without significant loss of their performance for at least 8 successive UV/dark cycles.