Abstract (EN):
The joining of Ti-47Al-2Cr-2Nb using Ti-15Cu-15Ni (wt%) as braze alloy was investigated. Experiments were conducted at 980 and 1000degreesC for 10 min. The microstructure and the chemical composition of the interfaces were studied by scanning electron microscopy (SEM) and by energy dispersive X-ray spectroscopy (EDS), respectively. For both processing conditions the reaction between the gamma-TiAl alloy and the braze alloy produced layered interfaces, which are essentially composed of alpha(2)-Ti3Al and of Ti-Ni-Cu-Al and Ti-Ni-Cu intermetallic compounds. Microhardness tests showed that all reaction layers are harder than either the gamma or the (alpha(2)+gamma) lamellar grains of the intermetallic alloy. (C) 2003 Kluwer Academic Publishers.